NRC to examine concrete degradation at Seabrook

17 September 2012

The Nuclear Regulatory Commission will conduct additional inspections and reviews to independently verify and assess work being done to address concrete degradation identified at the Seabrook nuclear power plant in New Hampshire. The 1295 MWe Seabrook pressurized water reactor is operated by NextEra Energy Seabrook, LLC.

NRC said in a statement that while its reactor oversight process does not prescribe increased oversight, “the (agency) staff believes the additional inspections and assessments are needed to support the review of licensee commitments and planned large-scale concrete specimen testing by the licensee, the development of staff technical guidance, and stakeholder communications and outreach activities,” as outlined in a memorandum.

That request for further resources has now been approved via the “Deviation Memorandum,” which refers to a deviation from the reactor oversight process.

The degradation of concrete in some areas of specific structures at the Seabrook plant is being caused by an alkali silica reaction. ASR is a chemical combining of reactive silica from the concrete aggregate with the alkali from the cement paste in the presence of moisture. The result of the reaction is a gel, which can expand and may cause micro-cracks in the concrete.

While the extent of the problem at Seabrook is still being evaluated, the NRC has determined that the structures identified to be affected by ASR can perform their safety function when called upon.


Related Articles
Noda calls for reduction of nuclear in Japan, where only three reactors remain in operation
Japan evaluates reprocessing options
Kan calls for Japan to phase out nuclear power
Japan plans to limit reactor lifetime to 40 years



Privacy Policy
We have updated our privacy policy. In the latest update it explains what cookies are and how we use them on our site. To learn more about cookies and their benefits, please view our privacy policy. Please be aware that parts of this site will not function correctly if you disable cookies. By continuing to use this site, you consent to our use of cookies in accordance with our privacy policy unless you have disabled them.